VESTAKEEP® 2000 CF30 | PEEK-CF30 | Evonik Operations GmbH
Release time：2025-06-18Author：小编
VESTAKEEP® 2000 CF30 | PEEK-CF30 | Evonik Operations GmbH
Product Texts
Carbon fiber-reinforced, medium viscosity polyether ether ketone
VESTAKEEP® 2000 CF30 is a medium-viscosity, carbon fiber-reinforced (30%) polyether ether ketone for injection molding.
The semi-crystalline polymer features superior, mechanical, thermal and chemical resistance. Parts made from VESTAKEEP® 2000 CF30 are of low flammability.
VESTAKEEP® 2000 CF30 can be processed by common injection machines for thermoplastics.
We recommend a melt temperature between 380°C and 400°C during the injection molding process. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C.
VESTAKEEP® 2000 CF30 is supplied as granules in 25 kg boxes with moisture-proof polyethylene liners.
Inside the original and undamaged packaging, the product has a shelf life of at least 2 years when stored in dry rooms at temperatures not exceeding 30°C.
Pigmention may effect values.
For information about processing of VESTAKEEP® 2000 CF30, please follow the general recommendations in our brochure “VESTAKEEP® PEEK-Processing Guidelines“.
The values presented are typical or average values, they do not constitute a specification.
| Rheological properties | Value | Unit | Test Standard |
| Melt volume-flow rate, MVR | 19 | cm³/10min | ISO 1133 |
| Temperature | 400 | °C | ISO 1133 |
| Load | 5 | kg | ISO 1133 |
| Molding shrinkage, parallel | 0 | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 0.4 | % | ISO 294-4, 2577 |
| Mechanical properties | Value | Unit | Test Standard |
| Tensile modulus | 24000 | MPa | ISO 527-1/-2 |
| Stress at break | 251 | MPa | ISO 527-1/-2 |
| Strain at break | 1.85 | % | ISO 527-1/-2 |
| Charpy impact strength, +23°C | 51C | kJ/m² | ISO 179/1eU |
| Charpy impact strength, -30°C | 45C | kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, +23°C | 8C | kJ/m² | ISO 179/1eA |
| Charpy notched impact strength, -30°C | 8C | kJ/m² | ISO 179/1eA |
| Thermal properties | Value | Unit | Test Standard |
| Melting temperature, 10°C/min | 340 | °C | ISO 11357-1/-3 |
| Glass transition temperature, 10°C/min | 146 | °C | ISO 11357-1/-2 |
| Temp. of deflection under load, 1.80 MPa | 330 | °C | ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa | 340 | °C | ISO 75-1/-2 |
| Vicat softening temperature, 50°C/h 50N | 340 | °C | ISO 306 |
| Coeff. of linear therm. expansion, parallel | 10 | E-6/K | ISO 11359-1/-2 |
| Burning behavior at 1.5 mm nominal thickness | V-0 | class | IEC 60695-11-10 |
| Thickness tested (1.5) | 1.6 | mm | IEC 60695-11-10 |
| Yellow Card available | Yes | - | - |
| Oxygen index | 47 | % | ISO 4589-1/-2 |
| Electrical properties | Value | Unit | Test Standard |
| Relative permittivity, 1MHz | 17 | - | IEC 62631-2-1 |
| Dissipation factor, 1MHz | 2300 | E-4 | IEC 62631-2-1 |
| Volume resistivity | 10000 | Ohm*m | IEC 62631-3-1 |
| Other properties | Value | Unit | Test Standard |
| Water absorption | 0.4 | % | Sim. to ISO 62 |
| Density | 1410 | kg/m³ | ISO 1183 |
| Test specimen production | Value | Unit | Test Standard |
| Injection molding, melt temperature | 380 | °C | ISO 294 |
| Injection molding, mold temperature | 180 | °C | ISO 294 |
| Injection molding, injection velocity | 200 | mm/s | ISO 294 |
| Injection molding, pressure at hold | 120 | MPa | ISO 294 |